Abstract This study evaluated the influence of heating temperature variability on the degradation level of concrete by varying the exposure temperatures (200°C, 450°C, and 800°C) and concrete design strength (C25 and C40). The concretes were submitted to ultrasound tests (before and after heating) and then were ruptured by axial compression. After rupture, samples were taken from the fracture section of the specimens for microstructural analysis by scanning electron microscope (SEM), and molecular analysis by Raman spectroscopy. The results showed that the residual strength of the concrete can change significantly (values differing by more than 100%) with temperature variability in the oven. There were physicochemical changes in the concrete constituents. The variations in Raman spectra and morphological changes (SEM images) allowed to analyze the variation in the level of degradation of concrete after exposure to fire, at the same firing step, due to temperature variation in the ovens, being compatible with the results of compressive strength and ultrasonic wave propagation velocity (UPV). Thus, the study highlights the need for adequate mapping of the heat in the oven and monitoring of the temperature of specimens in studies of concrete at high temperatures.

Resumo Este estudo avaliou a influência da variabilidade da temperatura de aquecimento no nível de degradação de concretos, variando-se temperatura de exposição (200°C, 450°C e 800°C) e resistência de projeto do concreto (C25 e C40). Os concretos foram submetidos a ensaios de ultrassom (antes e depois do aquecimento), e, posteriormente, foram rompidos à compressão axial. Após a ruptura foram retiradas amostras da seção de fratura dos corpos de prova para análises microestruturais, por microscópio eletrônico de varredura (MEV), e análises moleculares, por espectroscopia Raman. Os resultados mostraram que a resistência residual dos concretos pode mudar de maneira significativa (valores divergindo em mais de 100%) com a variabilidade de temperatura no forno. Houve alterações físico-químicas dos constituintes do concreto. As variações nos espectros Raman e as alterações morfológicas (imagens em MEV) permitiram verificar a variação do nível de degradação do concreto após exposição ao fogo, em uma mesma etapa de queima, devido variação de temperatura nos fornos, sendo compatíveis com os resultados de resistência à compressão e com os de ultrassom (velocidade do pulso ultrassônico). Dessa forma, o estudo evidencia a necessidade do mapeamento adequado do calor no forno e do monitoramento da temperatura dos corpos de prova, em estudos sobre concretos sob altas temperaturas.

Abstract Maraging steels are a class of ultra high strength steels of special importance due to their extremely high mechanical strength and good toughness. In this work, the effects of the solution annealing temperature on the mechanical properties of the maraging 300 steels were evaluated, in order to maximize the toughness without considerable detriment of the mechanical strength. Five solution annealing temperatures were evaluated. The characterization of the mechanical properties was done by tests of Rockwell C hardness, Charpy-V impact toughness, and tensile and fracture toughness in plane strain. The results obtained show that the fracture toughness increases, and the tensile strength decreases with the temperature of the solution annealing. In this way it was possible to find a heat treatment condition in which it was possible to raise about 20% of the toughness with a loss of only 6% in the tensile strength.

Resumo O uso das fibras da taboa (Typha latifolia Linn), para confecção de geotêxteis, tem sido trabalhada, buscando a estabilização de taludes de rios ou encostas, e assim criando um ambiente ecologicamente favorável para a recuperação da vegetação e a ancoragem do solo. O objetivo deste trabalho foi avaliar a resistência e durabilidade de geotêxteis fabricados com fibras da taboa submetidos ao envelhecimento acelerado em laboratório e degradação dessas fibras em campo. A confecção dos geotêxteis foi realizada com diferentes nós em fibras que passaram previamente por processos de secagem distintos. Para a realização dos testes em laboratório, foi construído aparato que permitiu submeter os corpos de prova ao envelhecimento precoce, buscando simulação das condições ambientais, isto é, as fibras foram expostas à radiação UVB seguida de condensação, utilizando-se também um resfriador mecânico para equalização da temperatura. Os ensaios de resistência à tração seguiram diretrizes observadas nas normas ISO 10319 (1996) e ISO 12236 (1998). Os ensaios de campo foram conduzidos por disposição de amostras em um talude da margem direita do rio São Francisco no município de Amparo do São Francisco-SE, 10°08'20.7"S 36°54'47.0"W, Nordeste do Brazil, com área de 20m2, submetidas às condições climáticas locais, para posterior avaliação da sua degradação. Uma vez que os materiais não apresentam homogeneidade na sua fabricação, ocorreram resultados não uniformes quando submetidos à degradação. Isso pode explicar o fato de serem observados aumentos inesperados nos valores de tensão e deformação. O geotêxteis de taboa apresentou resultados de tensão de ruptura e deformação que sinaliza positivamente para o seu uso comercial, confirmando, assim, as suas potencialidades para uso como parte das técnicas de bioengenharia de solos.

Abstract The use of taboa fibers (Typha latifolia Linn), for geotextile manufacturing, was designed to stabilize riverbanks or slopes and to create an ecologically suitable environment for the recovery of vegetation and soil anchoring. The objective of this work was to evaluate the resistance of geotextiles manufactured from taboa fibers submitted to accelerate aging in the laboratory and degradation of these fibers in the field. The geotextile manufacturing was performed with different knots in fibers that had previously undergone different drying processes. To perform the tests in the laboratory, an apparatus that allowed the geotextile to be subjected to premature aging was built, seeking to simulate the environmental conditions. The fibers were exposed to UVB radiation followed by condensation, using also a mechanical cooler, for temperature equalization. The tensile strength tests followed the guidelines observed in the ISO 10319 (1996) and ISO 12236 (1998) Brazilian National Standards. The field trials were conducted by placing samples on a slope on the right bank of the São Francisco river in the municipality of Amparo do São Francisco, Sergipe state, 10°08'20.7"S 36°54'47.0"W, Northeaster Brazil, with 20m2 area, under local climatic conditions, for further evaluation of their degradation. Since the materials are not homogeneous in their manufacture, non-uniform results occurred when subjected to degradation. This may explain the fact that unexpected increases in stress and strain values were observed. The taboa geotextile showed results of rupture stress and deformation that signals positively for its commercial use, thus confirming its potential for use as part of soil bioengineering techniques.

RESUMO A procura por compósito biodegradável vem crescendo mundialmente nos últimos anos, principalmente com o intuito de reduzir a contaminação ambiental por materiais estruturais produzidos a partir de derivados de petróleo. O objetivo deste estudo foi avaliar o crescimento de isolados do cogumelo comestível “Shiitake” (Lentinula edodes) em substrato à base de pó de coco suplementado com farelos, bem como analisar a influência do período de cultivo dos fungos e tempo de secagem do substrato colonizado nas propriedades mecânicas do compósito, visando a produção de compósito biodegradável. A densidade micelial não é influenciada pelo tipo de hifa dos isolados de L. edodes. A secagem do compósito não influencia no odor residual do compósito, a depender do isolado. A tensão compressiva e o tipo de espuma de compósitos fúngicos podem ser influenciados pelo período de cultivo e pelo tipo de hifa, a depender do isolado. Os compósitos colonizados pelos isolados de L. edodes apresentam maior resistência mecânica aos 30 dias da completa colonização. O pó de coco suplementado com farelo de trigo e colonizado pelo isolado fúngico LED 96/18 é uma alternativa ecológica na produção de embalagens considerando as propriedades mecânicas.

ABSTRACT The demand for biodegradable composite has grown worldwide in recent years, mainly in order to reduce environmental contamination by structural materials produced from the oil industry. The objective of this study was to evaluate the growth of isolates from the edible mushroom “Shiitake” (Lentinula edodes) in substrate coconut powder-based supplemented with wheat bran, as well as to analyze the influence of fungi growing period and drying time of the colonized substrate on the mechanical properties of the composite, in order to produce a biodegradable composite. The mycelial density is not influenced by the type of hyphae of L. edodes. Drying of the composite does not influence the residual odor, depending on the isolate. The compressive strength and foam type of the fungal composite may be influenced by the culture period and type of hyphae, depending on the fungal isolate. The composites colonized by the L. edodes isolates presented higher mechanical resistance at 30 days of complete colonization. The coconut powder supplemented with wheat bran colonized by isolated fungi LED 96/18 is an ecological alternative in the packaging production considering its mechanical properties.

RESUMO A produção de embalagens plásticas cresce mundialmente, o que resulta no acúmulo destes materiais no ambiente devido ao descarte inadequado e por serem de difícil decomposição. De forma alternativa, os compósitos produzidos com resíduos agrícolas e fungos filamentosos podem apresentar propriedades físicas e mecânicas similares ou superiores ao poliestireno expandido, a depender da espécie fúngica e do substrato de cultivo. Na literatura, não foram encontrados relatos sobre o emprego de pó de coco e fungos comestíveis de podridão branca nas propriedades mecânicas de compósitos. Assim, o objetivo deste trabalho foi selecionar isolados fúngicos e avaliar o período de cultivo na resistência mecânica de compósitos produzidos em pó de coco suplementado com farelo de trigo. O delineamento experimental utilizado foi inteiramente ao acaso em esquema fatorial 5 x 3 correspondente ao cultivo de cinco isolados fúngicos comestíveis (Pleurotus ostreatus - POS-W, POS-SP1 e POS-98/38; Pleurotus eryngii - POS ER e Pycnoporus sanguineus - PS) e três períodos de cultivo após a completa colonização do substrato (15, 30 e 45 dias), com quatro repetições. O período de cultivo dos isolados fúngicos pode influenciar na perda de massa e de volume do compósito. A resistência à compressão e a tenacidade do compósito são influenciadas pelo isolado fúngico e pelo tempo de cultivo do fungo. Os isolados de Pycnoporus sanguineus, de Pleurotus ostreatus e P. eryngii apresentam características para produção de compósitos biodegradáveis.

ABSTRACT The production of plastic packing grows worldwide, resulting in the accumulation of these materials in the environment due to improper disposal and problems related to degradation. Alternatively, composites produced with agricultural residues and filamentous fungi may exhibit physical and mechanical properties similar to or greater than expanded polystyrene, depending on the fungal species and substrate of the cultivation. In the literature, no reports were found on the use of coconut powder and edible fungi of white rot in the mechanical properties of composites. Thus, the objective of this work was to select fungal isolates and to evaluate the period of cultivation in the mechanical resistance of composites produced in coconut powder supplemented with wheat bran. The experimental design was completely randomized in a 5 x 3 factorial scheme corresponding to the cultivation of five edible fungal isolates (Pleurotus ostreatus: POS-W, POS-SP1, POS-98/38; Pleurotus eryngii: POS ER and Pycnoporus sanguineus: PS) and three culture periods after complete colonization of the substrate (15, 30 and 45 days), with four replications. The period of cultivation of the fungal isolates may influence in the composite mass loss and volume loss. The compressive strength and tenacity of the composite are influenced by the fungal isolate and the time of cultivation. The isolates of Pycnoporus sanguineus, Pleurotus ostreatus and P. eryngii present potential characteristics for the production of biodegradable composites.

Resumo Contexto O estudo do fenômeno de fadiga é essencial porque as falhas de implantes geralmente são causadas por este processo. Objetivo O objetivo deste estudo foi analisar a resistência à fadiga de conjuntos de pilares retos e anatômicos que foram submetidos a cargas cíclicas. Material e método Foram utilizados 37 implantes cone Morse e 37 pilares, divididos em dois grupos (n = 16: pilares retos, n = 21: pilares anatômicos). Os conjuntos foram submetidos à carga cíclica (5.000.000) usando o equipamento servo-hidráulico. Três conjuntos de cada grupo foram submetidos a testes de flexão para determinar a resistência de carga máxima, o que serviu de parâmetro para comparação dos testes cíclicos. Foram avaliados número de ciclos, carga e momento de flexão. Resultado Dos 31 pilares ciclicamente testados, 17 (54,8%) fraturaram em menos de 5 milhões de ciclos; 8 (25,8%) destes eram pilares retos, e 9 (29%) eram anatômicos. Um total de 14 amostras (45,2%) resistiu à carga cíclica. De acordo com o teste exato de Fisher, não houve diferença entre os grupos quanto à fratura. Conclusão Apesar dos pilares retos terem maior carga média e momento de flexão que os anatômicos, os dois tipos de pilares apresentaram desempenho semelhante quanto a resistência à fratura in vitro.

Abstract Background The study of the phenomenon of fatigue is essential because implant failures usually are caused by this process. Purpose The objective of this study was to examine the fatigue resistance of straight and anatomical abutments joints that were submitted to cyclic loads. Material and method We used 37 Morse taper implants and 37 abutments, divided into two groups (n= 16: straight abutment, n= 21 anatomical abutment). The sets were submitted to cyclic loading (5 million) using servo-hydraulic equipment. Three sets from each group were subjected to bending tests to determine the maximum load resistance, which served as the parameter for comparison of the cyclic tests. We evaluated number of cycles, load and bending moment. Result Of the 31 abutments cyclically tested, 17 (54.8%) fractured in fewer than 5 million cycles; 8 (25.8%) of these were straight abutments, and 9 (29%) were anatomical. A total of 14 samples (45.2%) resisted the cyclic loading. According to Fisher's exact test, there was no difference between groups as the fracture. Conclusion Despite of the straight abutments have higher average load and bending moment on the anatomical, both types of abutments showed similar performance as the fracture strength in vitro.

RESUMO OBJETIVOS: Estudo da remoção de haste do tipo force-closed e a sua reinserção posterior para aumentar a exposição do acetábulo durante a revisão. Não é conhecido o quanto esse procedimento modifica a interface haste/cimento. MÉTODOS: Três modelos de hastes afiladas foram implantadas em fêmures compósitos. Extensômetros de deformação foram embebidos no aspecto medial do manto de cimento e em diversas posições sobre a superfície externa dos fêmures. As deformações foram medidas durante cargas estáticas, as quais foram aplicadas em dois diferentes momentos: após a implantação e após um milhão de ciclos de carga, seguido pela remoção e reinserção. O teste t foi feito. As diferenças entre as deformações foram confrontadas com p ≤ 0,05 entre os dois momentos de carga estática e entre os três projetos de hastes. RESULTADOS: Não foram encontradas diferenças significativas nas deformações após os dois momentos de carga para os três modelos. Não foram encontradas diferenças significativas nas deformações iniciais dos três modelos para a maioria dos extensômetros aderidos aos fêmures. CONCLUSÕES: A reinserção de haste do tipo force-closed não altera a transmissão de carga da haste para o cimento e para a superfície do fêmur, mesmo após um milhão de ciclos.

ABSTRACT OBJECTIVES: This study investigated removal of a force-closed stem, done in order to improve acetabular exposure during revision, with reinsertion afterwards. It is unknown how much this procedure modifies the stem/cement interface. METHODS: Three tapered stem models were implanted into composite femurs. Strain gauges were embedded in the medial aspect of the cement mantle and in several positions on the outer surface of the femurs. The deformation was measured during static loading, which was applied at two different times: after implantation and after one million loading cycles, followed by stem removal and reinsertion. The t test was performed. The differences in deformation were compared (at p ≤ 0.05) between the two static loading times and among the three stem designs. RESULTS: No significant differences in deformation were found after the two loading times for the three models. No significant differences in the initial deformations of the three models were found for most of the gauges attached to the femurs. CONCLUSIONS: Reinsertion of the force-closed stem does not alter the load transmission from the stem to the cement and to the surface of the femur, even after one million loading cycles.

RESUMO OBJETIVOS: Diferenças sutis no projeto da haste podem resultar em diferentes respostas mecânicas da artroplastia total do quadril. Testes que meçam a migração da haste em relação ao fêmur, bem como as deformações no cimento e no fêmur, podem salientar as diferenças entre diferentes projetos de hastes. MÉTODOS: Neste artigo foram implantadas hastes cônicas, hastes duplamente afiladas e triplamente afiladas em fêmures compósitos e submetidas a cargas estáticas e cíclicas. As hastes diferenciaram-se principalmente em relação aos afilamentos, ao raio do calcar e à rigidez proximal. A migração das hastes e as deformações tanto no fêmur quanto no cimento foram medidas. RESULTADOS: Foram observadas diferenças significativas (p < 0,05) na rotação permanente entre as hastes duplamente e triplamente afiladas, nas deformações do nível proximal medial do fêmur entre as hastes triplamente afiladas e ambas cônicas e duplamente afiladas e nas deformações do nível proximal lateral do fêmur entre as hastes duplamente afiladas e ambas cônicas e triplamente afiladas. CONCLUSÃO: Os ensaios mecânicos propostos foram capazes de produzir diferenças significativas no comportamento dessas hastes semelhantes. A rigidez proximal da haste e o raio do calcar influenciam a estabilidade rotacional e a transmissão de deformação da haste ao femur.

ABSTRACT Objectives: Subtle differences in stem design can result in different mechanical responses of the total hip arthroplasty. Tests measuring migration of the stem relative to the femur, as well as the strains in the cement mantle and on the femur can detect different mechanical behavior between stems. Methods: In this article, conical, double and triple tapered stems were implanted in composite femurs and subjected to static and cyclic loads. Stems differed mainly on taper angle, calcar radius and proximal stiffness. Stem migration and strains on the femur and in the cement mantle were achieved. Results: Significant differences (p < 0.05) were noted in the permanent rotation between double and triple tapers, in the strains on the proximal medial femur between triple and both conical and double tapers, and in the strains on the lateral proximal femur between double tapers and both conical and triple tapers. Conclusion: The proposed mechanical tests were able to detect significant differences in the behavior of these resembling stems. Stem proximal stiffness and the calcar radius of the stem influence its rotational stability and the strain transmission to the femur.

ResumoIntroduçãoO cimento resinoso dual é o principal material para cimentação de cerâmicas. Contudo, fatores, como fonte de luz, podem influenciar no desempenho do cimento.ObjetivoAvaliar a influência de duas fontes de luz de diferentes intensidades sobre a microdureza de um cimento resinoso quando fotoativado sob diferentes cerâmicas.Material e métodoForam fotoativados 40 espécimes de cimento resinoso dual (10 mm × 1,0 mm) por meio de duas fontes de luz LED, com intensidades de 1.000 mW/cm² e 800 mW/cm² durante 40 segundos, sob cerâmicas (15 mm × 2 mm) à base de zircônia, espinélio MgAl2O4 e dissilicato de lítio. No grupo controle, foi utilizada uma placa de vidro de mesma dimensão. As amostras tiveram a superfície regularizada com lixa d`água (600 e 1200). Após armazenagem a seco no escuro (24 h), foram realizadas as medidas de microdureza Vickers (HMV Shimadzu - 50g/10 segundos). Os dados foram submetidos à Anova fatorial e ao teste de Tukey com nível de significância de 5%.ResultadoO cimento polimerizado apresentou valor médio de microdureza e desvio padrão para o grupo controle de 43,9±1,5 e 43,4±1,3, para as intensidades de 1.000 mW/cm2 e 800 mW/cm2, respectivamente. O menor valor de microdureza do cimento foi observado para a cerâmica à base de espinélio MgAl2O4, polimerizado a 800 mW/cm², com valor de 34,3±3,3.ConclusãoO tipo de cerâmica e a intensidade da fonte de luz influenciam na microdureza do cimento. A intensidade de 1.000 mW/cm2 sobre as cerâmicas à base de zircônia e espinélio MgAl2O4 resultaram na melhor combinação de valores de dureza do cimento.

AbstractIntroductionThe dual-cure resin cement is the main material for luting of ceramic. However, factors such as light source can influence the performance of the cement.ObjectiveEvaluate the influence of two light sources of different intensities on the microhardness of a resin cement when cured under different ceramics.Material and methodForty samples of dual resin cement were photoactivated by two LED light sources, with light intensity of 1000mW/cm² and 800mW/cm², respectively (40 seconds), under the base ceramic Zirconia, Spinel MgAl2O4 and Lithium Disilicate. In the control group, a glass plate was used. Each samples had the surface grounded (600 and 1200). After dry storage in the dark (24 hours), Vickers microhardness measurements were performed (HMV Shimadzu - 50gf/10 seconds). The data were submitted to factorial ANOVA and Tukey's test with significance level of 5%.ResultThe average hardness and standard deviation in the control group for cement polymerized 1000mW/cm² was 43.9±1.5 and 800mW/cm² the value of 43.4±1.3. The lowest value was for the Ceramic base of spinel MgAl2O4, light cured with 800mW/cm² with a value of 34.3±3.3.ConclusionThe ceramic type and intensity of the light source influence the hardness of the cement. The polymerization 1000mW/cm2 on the ceramic based on zirconia and spinel MgAl2O4 resulted in the best combination of hardness cement.

Objetivo Analisar a resistência à fratura por fadiga dos conjuntos implante-pilar, nos tipos reto e angulado, submetidos a cargas cíclicas similares às mastigatórias. Material e método Foram utilizados 32 implantes (3,75 × 11 mm) com sistema cone Morse e 32 pilares, separados em dois grupos: pilares retos e angulados (n=16) (Neodent, Curitiba, PR, Brasil). Os conjuntos foram submetidos a testes cíclicos em equipamento servo-hidráulico, fixando-se o número de ciclos em cinco milhões. Foram avaliados: número de ciclos, carga e momento de força das amostras. O Teste de Fisher e o Teste ANOVA foram aplicados (p<0,005). Amostras fraturadas foram analisadas em microscopia eletrônica de varredura (MEV). Resultado Dos pilares retos, quatro resistiram ao número de ciclos estabelecidos, suportando cargas entre 470 N e 510 N. No grupo dos angulados, nove amostras resistiram a cargas entre 570 N e 890 N. Quanto às amostras fraturadas abaixo do número de ciclos, no grupo pilar reto, nove fraturaram com cargas entre 470 N e 630 N. No grupo pilar angulado, cinco amostras fraturaram com cargas entre 760 N e 890 N. Foi calculado, para cada conjunto implante-pilar, o momento de força (Médias: Grupo reto – 4.335,2 Nmm, Grupo angulado – 3.923,3 Nmm). Conclusão Os dois tipos de pilares (retos e angulados), em condições in vitro, comportaram-se estatisticamente de forma semelhante, sendo aceita a hipótese nula de que não há diferença de resistência à fratura entre os grupos.

Objective The aim of this study was to verify the fatigue fracture resistance of the implant-abutment joint, in straight and angled types, subject to cyclic loads similar to chewing. Material and method It was used 32 implants system (3.75 × 11mm) with Morse taper and 32 abutment, divided in two groups: abutment straight and angled (n = 16) (Neodent, Curitiba, PR, Brazil). The sets were submitted to cyclic testing using servo-hydraulic equipment, fixing the number of cycles at 5 million. It was evaluated the number of cycles, load and moment force of the samples. The Fisher test and ANOVA were applied (p<0,005). Fractured samples were analyzed in the scanning electron microscopy (SEM). Result Straight abutment, four resisted the cycles number established, supporting loads between 470N and 510N. Angled abutment: nine resisted to loads between 570N and 890N. Regarding the fractured samples below the number of cycles, in the straight abutment, nine fractured with loads between 470N and 630N. In the angled abutment, five fractured with loads ranging from 760N and 890N. The moment of the force was calculated for each joint implant-abutment (Averages: Straight Group - 4335,23Nmm, angled Group - 3923,37Nmm). Conclusion Two types of abutments (straight and angled), in vitro conditions, statistically behaved similarly, and accepts the null hypothesis that there is no difference in fracture resistance between groups.

This study examined the effect of deproteinization on the bond strength between self-adhesive resin cements and dentin surfaces that were untreated (control), acid-etched, or acid-etched and subjected to a post-etch deproteinization treatment. Cylinders of RelyX Unicem or BisCem (n = 6) cement were build-up on the dentin surfaces and tested to determine shear strength. The results were analyzed using two-way ANOVA and Tukey's test (5%). While neither dentin pretreatment improved the bond strength for RelyX Unicem, deproteinization treatments resulted in greater bond strength in BisCem specimens while acid etching alone did not improve the performance of the material.

INTRODUÇÃO: Apesar da importância da etapa de condicionamento ácido nos procedimentos adesivos, pouco se sabe sobre o efeito da marca do condicionador ácido sobre a união do adesivo à dentina. OBJETIVO: Este estudo avaliou o efeito de diferentes condicionadores ácidos na união da resina composta à dentina. MATERIAL E MÉTODO: Vinte e cinco incisivos bovinos tiveram a coroa dividida em duas hemissecções. As superfícies vestibulares foram desgastadas com lixa carbeto de silício (SiC) #180 até a exposição de dentina, seguida por lixas SiC #600 para padronização da smear layer. As amostras foram aleatoriamente alocadas em cinco grupos (n = 10), de acordo com marca do condicionador ácido: 3M ESPE, Ultradent, Dentsply, Villevie e DFL. Apenas um sistema de união convencional de dois passos (Ambar, FGM) foi utilizado. Matrizes de silicone foram utilizadas na confecção de três cilindros de resina composta em cada amostra. Após 24 horas, os cilindros foram testados sob carga de cisalhamento até a falha. Os dados foram analisados com ANOVA a um critério e teste de Tukey (a = 0,05). O modo de falha foi avaliado em microscopia óptica e os dados submetidos ao Teste Qui-quadrado (a = 0,05). RESULTADO: Não houve diferença estatística na resistência de união obtida entre os condicionadores ácidos avaliados. Houve predomínio de falhas adesivas, exceto para os condicionadores da Dentsply e DFL, que demonstraram similaridade entre falhas adesivas e mistas. CONCLUSÃO: As diferentes marcas de condicionadores ácidos avaliados não influenciaram a resistência de união de resina composta à dentina.

INTRODUCTION: Despite the importance of the acid etching step on bonding procedures, little is known about the acid etchant brand effect on bond strength of adhesive to dentin. OBJECTIVE: The aim of this study was to evaluate the effect of different acid etchants at the bond strength of composite resin to dentine. MATERIAL AND METHOD: Twenty five bovine incisors had their crown sectioned in two hemi-sections. The buccal surfaces were grounded with #180 silicon carbide (SiC) abrasive paper to exposure of dentin, followed by #600 SiC paper to standardize the smear layer. The samples were randomly allocated into five groups (n = 10) according to acid etchant brands: 3M ESPE, Ultradent, Dentsply, Villevie and DFL.Only a two-step etch-and-rinse adhesive system (Ambar, FGM) was used. Silicon molds were used to build-up three resin composite cylinder per sample. After 24 hours, cylinders were submitted to shear load until the failure. Data were analyzed by one way ANOVA and Tukey`s test (a = 0.05). The failure mode was evaluated under optical microscopy and the data were submitted to Chi-square test (a = 0.05). RESULT: There was no statistical difference on bond strength obtained between the acid etchants evaluated. There was predominance of adhesive failures, except for etchants of Dentsply and DFL that showed similarity between mixed and adhesive failures. CONCLUSION: Different brands of acid etchants did not influence on the bond strength of composite resin to dentin.